Cracking model for concrete

The Abaqus/Explicit cracking model assumes fixed, orthogonal cracks, with the maximum number of cracks at a material point limited by the number of direct stress components present at that material point of the finite element model (a maximum of three cracks in three-dimensional, plane strain, and axisymmetric problems; two cracks in plane stress and shell problems; and one crack in beam or truss problems). Internally, once cracks exist at a point, the component forms of all vector- and tensor-valued quantities are rotated so that they lie in the local system defined by the crack orientation vectors (the normals to the crack faces). The model ensures that these crack face normal vectors will be orthogonal, so that this local crack system is rectangular Cartesian. For output purposes you are offered results of stresses and strains in the global and/or local crack systems.

A simple Rankine criterion is used to detect crack initiation. This criterion states that a crack forms when the maximum principal tensile stress exceeds the tensile strength of the brittle material. Although crack detection is based purely on Mode I fracture considerations, ensuing cracked behavior includes both Mode I (tension softening/stiffening) and Mode II (shear softening/retention) behavior, as described later.

As soon as the Rankine criterion for crack formation has been met, we assume that a first crack has formed. The crack surface is taken to be normal to the direction of the maximum tensile principal stress. Subsequent cracks may form with crack surface normals in the direction of maximum principal tensile stress that is orthogonal to the directions of any existing crack surface normals at the same point.

Cracking is irrecoverable in the sense that, once a crack has occurred at a point, it remains throughout the rest of the calculation. However, crack closing and reopening may take place along the directions of the crack surface normals. The model neglects any permanent strain associated with cracking; that is, it is assumed that the cracks can close completely when the stress across them becomes compressive.

In reinforced concrete the specification of postfailure behavior generally means giving the postfailure stress as a function of strain across the crack (Figure 1). In cases with little or no reinforcement, this introduces mesh sensitivity in the results, in the sense that the finite element predictions do not converge to a unique solution as the mesh is refined because mesh refinement leads to narrower crack bands.

Figure 1. Postfailure stress-strain curve.

In practical calculations for reinforced concrete, the mesh is usually such that each element contains rebars. In this case the interaction between the rebars and the concrete tends to mitigate this effect, provided that a reasonable amount of “tension stiffening” is introduced in the cracking model to simulate this interaction. This requires an estimate of the tension stiffening effect, which depends on factors such as the density of reinforcement, the quality of the bond between the rebar and the concrete, the relative size of the concrete aggregate compared to the rebar diameter, and the mesh. A reasonable starting point for relatively heavily reinforced concrete modeled with a fairly detailed mesh is to assume that the strain softening after failure reduces the stress linearly to zero at a total strain about ten times the strain at failure. Since the strain at failure in standard concretes is typically 10⁻⁴, this suggests that tension stiffening that reduces the stress to zero at a total strain of about 10⁻³ is reasonable. This parameter should be calibrated to each particular case. In static applications too little tension stiffening will cause the local cracking failure in the concrete to introduce temporarily unstable behavior in the overall response of the model. Few practical designs exhibit such behavior, so that the presence of this type of response in the analysis model usually indicates that the tension stiffening is unreasonably low.

BRITTLE CRACKING, TYPE=STRAIN

Property module: material editor: 
MechanicalBrittle Cracking: Type: Strain

When there is no reinforcement in significant regions of the model, the tension stiffening approach described above will introduce unreasonable mesh sensitivity into the results. However, it is generally accepted that Hillerborg's (1976) fracture energy proposal is adequate to allay the concern for many practical purposes. Hillerborg defines the energy required to open a unit area of crack in Mode I ($G_f^I$) as a material parameter, using brittle fracture concepts. With this approach the concrete's brittle behavior is characterized by a stress-displacement response rather than a stress-strain response. Under tension a concrete specimen will crack across some section; and its length, after it has been pulled apart sufficiently for most of the stress to be removed (so that the elastic strain is small), will be determined primarily by the opening at the crack, which does not depend on the specimen's length.

Implementation

In Abaqus/Explicit this fracture energy cracking model can be invoked by specifying the postfailure stress as a tabular function of displacement across the crack, as illustrated in Figure 2.

Figure 2. Postfailure stress-displacement curve.

Alternatively, the Mode I fracture energy, $G_f^I$, can be specified directly as a material property; in this case, define the failure stress, ${\sigma }_{tu}^I$, as a tabular function of the associated Mode I fracture energy. This model assumes a linear loss of strength after cracking (Figure 3).

Figure 3. Postfailure stress-fracture energy curve.

The crack normal displacement at which complete loss of strength takes place is, therefore, $u_{n0}=2G_f^I/{\sigma }_{tu}^I$. Typical values of $G_f^I$ range from 40 N/m (0.22 lb/in) for a typical construction concrete (with a compressive strength of approximately 20 MPa, 2850 lb/in²) to 120 N/m (0.67 lb/in) for a high-strength concrete (with a compressive strength of approximately 40 MPa, 5700 lb/in²).

Input File Usage

Use the following option to specify the postfailure stress as a tabular function of displacement:

BRITTLE CRACKING, TYPE=DISPLACEMENT

Use the following option to specify the postfailure stress as a tabular function of the fracture energy:

BRITTLE CRACKING, TYPE=GFI

Abaqus/CAE Usage

Property module: material editor: 
MechanicalBrittle Cracking: Type: Displacement or GFI

This test is difficult to perform because it is necessary to have a very stiff testing machine to record the postcracking response. Quite often such equipment is not available; in this situation you must make an assumption about the tensile failure strength of the material and the postcracking response. For concrete the assumption usually made is that the tensile strength is 7–10% of the compressive strength. Uniaxial compression tests can be performed much more easily, so the compressive strength of concrete is usually known.

The values given for tension stiffening are a very important aspect of simulations using the Abaqus/Explicit brittle cracking model. The postcracking tensile response is highly dependent on the reinforcement present in the concrete. In simulations of unreinforced concrete, the tension stiffening models that are based on fracture energy concepts should be utilized. If reliable experimental data are not available, typical values that can be used were discussed before: common values of $G_f^I$ range from 40 N/m (0.22 lb/in) for a typical construction concrete (with a compressive strength of approximately 20 MPa, 2850 lb/in²) to 120 N/m (0.67 lb/in) for a high-strength concrete (with a compressive strength of approximately 40 MPa, 5700 lb/in²). In simulations of reinforced concrete the stress-strain tension stiffening model should be used; the amount of tension stiffening depends on the reinforcement present, as discussed before. A reasonable starting point for relatively heavily reinforced concrete modeled with a fairly detailed mesh is to assume that the strain softening after failure reduces the stress linearly to zero at a total strain about ten times the strain at failure. Since the strain at failure in standard concretes is typically 10⁻⁴, this suggests that tension stiffening that reduces the stress to zero at a total strain of about 10⁻³ is reasonable. This parameter should be calibrated to each particular case.

Calibration of the postcracking shear behavior requires combined tension and shear experiments, which are difficult to perform. If such test data are not available, a reasonable starting point is to assume that the shear retention factor, $\rho$, goes linearly to zero at the same crack opening strain used for the tension stiffening model.

The brittle failure criterion is a crude way of modeling failure in Abaqus/Explicit and should be used with care. The main motivation for including this capability is to help in computations where not removing an element that can no longer carry stress may lead to excessive distortion of that element and subsequent premature termination of the simulation. For example, in a monotonically loaded structure whose failure mechanism is expected to be dominated by a single tensile macrofracture (Mode I cracking), it may be reasonable to use the brittle failure criterion to remove elements. On the other hand, the fact that the brittle material loses its ability to carry tensile stress does not preclude it from withstanding compressive stress; therefore, it may not be appropriate to remove elements if the material is expected to carry compressive loads after it has failed in tension. An example may be a shear wall subjected to cyclic loading as a result of some earthquake excitation; in this case cracks that develop completely under tensile stress will be able to carry compressive stress when load reversal takes place.

Thus, the effective use of the brittle failure criterion relies on you having some knowledge of the structural behavior and potential failure mechanism. The use of the brittle failure criterion based on an incorrect user assumption of the failure mechanism will generally result in an incorrect simulation.

When you define brittle failure, you can control how many cracks must open to beyond the failure value before a material point is considered to have failed. The default number of cracks (one) should be used for most structural applications where failure is dominated by Mode I type cracking. However, there are cases in which you should specify a higher number because multiple cracks need to form to develop the eventual failure mechanism. One example may be an unreinforced, deep concrete beam where the failure mechanism is dominated by shear; in this case it is possible that two cracks need to form at each material point for the shear failure mechanism to develop.

Again, the appropriate choice of the number of cracks that must fail relies on your knowledge of the structural and failure behaviors.

It is possible to use the brittle failure criterion in brittle cracking elements for which rebar are also defined; the obvious application is the modeling of reinforced concrete. When such elements fail according to the brittle failure criterion, the brittle cracking contribution to the element stress carrying capacity is removed but the rebar contribution to the element stress carrying capacity is not removed. However, if you also include shear failure in the rebar material definition, the rebar contribution to the element stress carrying capacity will also be removed if the shear failure criterion specified for the rebar is satisfied. This allows the modeling of progressive failure of an under-reinforced concrete structure where the concrete fails first followed by ductile failure of the reinforcement.